主题：【求助】金属基体多孔氧化膜阻抗分析，实在拟合不出来了……（Zsimpwin）

威望太小，数据附件不可见，黏贴如下：
100000    18.92    -3.0117
69024    19.244    -2.6812
47644    19.375    -2.6135
32886    19.629    -2.6426
22699    19.963    -3.1781
15668    20.21    -3.7701
10815    20.539    -4.9346
7464.9    21.058    -6.4164
5152.6    21.665    -8.5199
3556.5    22.464    -11.508
2454.9    23.595    -15.733
1694.5    24.886    -21.134
1169.6    27.088    -28.815
807.31    29.842    -39.293
557.24    34.401    -53.096
384.63    39.157    -73.122
265.49    46.513    -100.34
183.25    54.459    -137.41
126.49    70.067    -183.18
87.309    99.001    -257.8
59.71    135.708    -411.22
40.14    139.77    -403.87
26.482    201.15    -670.52
17.117    298.66    -994.81
10.817    400.21    -1414.1
6.6698    568.5    -2102.4
4.0036    877.25    -3293.4
2.3341    1367    -5104.2
1.3186    2145.3    -8223.7
0.72052    4092.7    -16148
0.38032    5884.2    -23659
0.19392    10691.5    -42906
0.09568    18201    -76119
0.04589    34005    -140200
0.02154    61043    -257610
0.01    123640    -497430

我也有类似问题，你看看你的nyquest图，然后确定有否wurburg diffusion,考虑修改低频区间，控制电路中的原件或者参数