主题：【求助】这里有个TiO2的HRTEM图，请各位帮忙分析一下

原文由 princeasuka(princeasuka) 发表:
XRD分析表明是锐钛矿，卡号21-1272
FFT中为什么既有环又有斑点？？
环我标出一些，由内至外包括（101）（004）（105）（215）
但是斑点我不明白是什么，没有符合夹角的晶面。就指导~~谢谢~~

d(A)    I(f)  I(v)  h  k  l  n^2  2-Theta  Theta  1/(2d)  2pi/d   
3.520  100.0  100.0  1  0  1        25.281  12.640  0.1420  1.7850 
2.431  10.0  14.0  1  0  3        36.946  18.473  0.2057  2.5846 
2.378  20.0  30.0  0  0  4        37.800  18.900  0.2103  2.6422 
2.332  10.0  15.0  1  1  2        38.575  19.288  0.2144  2.6943 
1.892  35.0  65.0  2  0  0        48.049  24.024  0.2643  3.3209 
1.699  20.0  41.0  1  0  5        53.890  26.945  0.2941  3.6962 
1.666  20.0  42.0  2  1  1        55.060  27.530  0.3000  3.7703 
1.493    4.0    9.0  2  1  3        62.119  31.059  0.3349  4.2084 
1.480  14.0  33.0  2  0  4        62.688  31.344  0.3377  4.2431 
1.364    6.0  15.0  1  1  6        68.760  34.380  0.3665  4.6061 
1.337    6.0  16.0  2  2  0        70.309  35.154  0.3737  4.6967 
1.279    2.0    6.0  1  0  7        74.029  37.014  0.3908  4.9107 
1.264  10.0  28.0  2  1  5        75.029  37.515  0.3953  4.9673 
1.250    4.0  11.0  3  0  1        76.017  38.009  0.3997  5.0229 
1.189    2.0    6.0  0  0  8        80.725  40.362  0.4204  5.2827 
1.172    2.0    6.0  3  0  3        82.136  41.068  0.4264  5.3588 
1.166    6.0  18.0  2  2  4        82.659  41.330  0.4287  5.3868 
1.160    4.0  12.0  3  1  2        83.146  41.573  0.4307  5.4128 
1.060    2.0    7.0  2  1  7        93.217  46.609  0.4717  5.9275 
1.051    4.0  13.0  3  0  5        94.178  47.089  0.4754  5.9743 
1.043    4.0  13.0  3  2  1        95.139  47.570  0.4791  6.0207 
1.018    2.0    7.0  1  0  9        98.315  49.158  0.4911  6.1709 
1.007    2.0    7.0  2  0  8        99.801  49.900  0.4965  6.2395 
0.996    2.0    7.0  3  2  3      101.217  50.609  0.5017  6.3040 
0.955    4.0  15.0  3  1  6      107.444  53.722  0.5233  6.5758 
0.946    4.0  15.0  4  0  0      108.959  54.479  0.5283  6.6390 
0.924    2.0    8.0  3  0  7      112.836  56.418  0.5408  6.7956 
0.919    2.0    8.0  3  2  5      113.857  56.928  0.5440  6.8355 
0.913    2.0    8.0  4  1  1      114.904  57.452  0.5472  6.8759 
0.896    4.0  16.0  2  1  9      118.434  59.217  0.5577  7.0078 
0.889    2.0    8.0  2  2  8      120.099  60.049  0.5624  7.0677 
0.881    2.0    8.0  4  1  3      121.720  60.860  0.5670  7.1246 
0.879    2.0    8.0  4  0  4      122.331  61.165  0.5686  7.1457 
0.846    2.0    8.0  4  2  0      131.029  65.514  0.5907  7.4234 
0.830    2.0    8.0  3  2  7      135.991  67.996  0.6018  7.5628 
0.826    4.0  17.0  4  1  5      137.384  68.692  0.6047  7.5994 
0.810    2.0    9.0  3  0  9      143.878  71.939  0.6171  7.7551 
0.797    4.0  18.0  4  2  4      150.028  75.014  0.6270  7.8796 
0.792    2.0    9.0  0  0  12      152.622  76.311  0.6307  7.9253 

原文由 princeasuka(princeasuka) 发表:
这里还有同一样品的另一张HRTEM的FFT

原文由 咖啡无糖(taboo) 发表:
这图中的环是非晶环 如果斑点对不上

高分辨的小区域的话 可以考虑其他的TiOx结构的可能性

不过 建议做一下大区域的SAED 标一下衍射环

先确定一下 可能存在的结构

原文由 小M Orz=3(mitchell_dyzy) 发表:

原文由 咖啡无糖(taboo) 发表:
这图中的环是非晶环 如果斑点对不上

高分辨的小区域的话 可以考虑其他的TiOx结构的可能性

不过 建议做一下大区域的SAED 标一下衍射环

先确定一下 可能存在的结构

请教一下，多晶的环是什么样的？和非晶环有何区别？

原文由 w4m0330(w4m0330) 发表:
FFT中的环是非晶的环，焦距不同的时候这些环的形状也会不同，对应于通频带的移动。不用去管环，直接找点就好了

原文由 小M Orz=3(mitchell_dyzy) 发表:

原文由 咖啡无糖(taboo) 发表:
这图中的环是非晶环 如果斑点对不上

高分辨的小区域的话 可以考虑其他的TiOx结构的可能性

不过 建议做一下大区域的SAED 标一下衍射环

先确定一下 可能存在的结构

请教一下，多晶的环是什么样的？和非晶环有何区别？